Lara Jimenez, CarolinaCarolinaLara JimenezDr. Arango Mejía, Jorge HernandoDra. Malkun, Soraya2026-04-082026-04-081998-05-18https://repositorio.unicoc.edu.co/handle/SII-Unicoc/1916The purpose of this study was to measure the bond strength of porcelain to commercially pure titanium (cp Ti) using different surface treatments (oxidation time and temperature). One hundred and twenty cp Ti sheets were obtained and divided into 12 groups according to the surface treatment. After porcelain placement, the sheets were subjected to a three-point load test until the porcelain detached. The results were evaluated by ANOVA (95% confidence level) and with the SAS and Tukey tests. No statistically significant differences were found between the different surface treatments.El propósito de este estudio fue medir la resistencia adhesiva de la porcelana al Titanio comercialmente puro (Ti cp) utilizando diferentes tratamientos de superficie (Tiempo y Temperatura de Oxidación). Se obtuvieron 120 láminas de Ti cp las cuales fueron divididas de acuerdo con el tratamiento de superficie en 12 grupos. Después de la colocación de la porcelana fueron sometidas a carga por medio de la prueba de los tres puntos hasta que se desprendiera la porcelana. Los resultados fueron evaluados por ANOVA (nivel de confianza 95%) y con método de comprobación SAS y Tukey. No se encontraron diferencias estadísticamente significativas entre los diferentes tratamientos de superficie.72 pp.application/pdfesSistema De PorcelanaInvestigación de campotext::thesis::bachelor thesisTPR 00007Porcelain SystemopenAccess